Yb valence in YbMn 2 (Si,Ge) 2 J.M. Cadogan and D.H. Ryan Department of Physics and Astronomy, University of Manitoba Winnipeg, MB, R3T 2N2, Canada E-mail: cadogan@physics.umanitoba.ca Department of Physics, McGill University Montreal, QC, H3A 2T8, Canada E-mail: dhryan@physics.mcgill.ca.

alagan
Download Presentation

Previous work

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Yb valence in YbMn2(Si,Ge)2J.M. Cadogan and D.H. RyanDepartment of Physics and Astronomy, University of ManitobaWinnipeg, MB, R3T 2N2, Canada E-mail: cadogan@physics.umanitoba.caDepartment of Physics, McGill UniversityMontreal, QC, H3A 2T8, Canada E-mail: dhryan@physics.mcgill.ca

  2. Nowik et al. [1] used magnetometry and 57Fe Mössbauer (on doped samples) to show that the Mn sublattice in YbMn2Si2 is antiferromagnetic (AF) below 520 K. A further transition at 35 K was attributed to a possible magnetic ordering of the Yb3+ sublattice. YbMn2Ge2 was shown to order at 495 K and to exhibit multiple magnetic transitions at lower temperatures. Yb was suggested to be divalent in the germanide, on the basis of cell-volume considerations. Subsequent neutron diffraction work by Hofmann et al. [2-4] showed that YbMn2Ge2 is a planar AF below 510 K and exhibits spin-canting below 185 K. No ordering of the Yb sublattice was detected. Analysis of the T-dependence of the lattice parameters led to the suggestion that the Yb ion has a valence of 2.35 in the germanide. Neutron diffraction indicated that the silicide orders in an axial AF structure below 526 K. The ‘event’ at 35 K was shown to be due to a rearrangement of the Mn moments into a cell-doubled AF state. The Yb3+ moments ordered below 10 K. Electronic structure determinations by XPS were interpreted by Szytula et al. [5] as showing Yb to be trivalent in the silicide and divalent in the germanide. Previous work

  3. Mn is the only transition metal to carry a magnetic moment in the RT2X2 series. Ytterbium is a Lanthanide (“Rare-Earth” R) element with an atomic number of 70. The most common ionization state for R ions is 3+, leaving Yb3+ with an outer electron configuration of 4f13, one electron short of a full 4f shell. Thus, we have the possibility of valence fluctuations or a mixed valence state since Yb2+ would have a 4f14 configuration i.e. a full 4f shell. Mössbauer spectroscopy can easily distinguish between Yb3+ and Yb2+ Yb3+ has both a magnetic moment and a 4f contribution to the electric field gradient at the 170Yb nucleus; the full-4f-shell of Yb2+ has neither. YbMn2(Si,Ge)2

  4. Mössbauer Spectroscopyof 170Yb The 84.2 keV Mössbauer gamma-ray arises from the transition between the I=2 excited nuclear state and the I=0 ground state of the 170Yb nucleus. 170Tm 130 d b– I=2 84.2 keV, 1.6 ns 0 keV I=0 170Yb

  5. YbMn2(Si,Ge)2 samples were prepared by arc-melting The crystal structure of YbMn2(Si,Ge)2 is body-centred tetragonal ThCr2Si2-type with the I4/mmm space group (#139) The Yb ions occupy the 2a sites with the point-group 4/mmm. Mn occupies the 4d sites and Si/Ge occupies the 4e sites. The 10 mCi 170Tm Mössbauer source was prepared by neutron activation of 25 mg of Tm as a 10 wt-% alloy in Aluminium. The source and sample were mounted vertically in a helium cryostat and the Mössbauer drive was operated in sine mode. The 84.2 keV Mössbauer g-rays were detected with a HPGe detector. The drive was calibrated with a laser interferometer. Experimental details Yb Mn Si,Ge

  6. 170Yb Mössbauer spectra Yb2+(small EFG) YbMn2Si2-xGex All spectra were fitted using a non-linear, least-squares minimization routine with line positions and intensities derived from an exact solution to the full Hamiltonian [6]. x Yb3+ (larger EFG due to 4f contribution)

  7. Relative fractions of Yb2+ and Yb3+ in YbMn2(Si,Ge)2 Determined from the relative areas of the magnetic (3+) and non-magnetic (2+) spectral components 2+ 3+ x

  8. Conclusion References 170Yb Mössbauer spectroscopy provides a direct and unambiguous determination of the valence of the Yb ion in the YbMn2(Si,Ge)2 family of intermetallics. [1] I. Nowik et al. J. Magn. Magn. Mater. 185 91-3 (1998) [2] M. Hofmann et al. J. Alloys Comp. 311 137-42 (2000) [3] M. Hofmann et al. J. Phys.: Condens. Matter 13 9773-80 (2001) [4] M. Hofmann et al. Appl. Phys A74 S713-5 (2002) [5] A. Szytula et al. J. Alloys Comp. 366 313-8 (2004) [6] D.H. Ryan et al. J. Phys.: Condens. Matter 16 6129-38 (2004)