An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. High-performance 4H-SiC-based ultraviolet p-i-n photodetectorXiaping Chen, Huili Zhu, and Jiafa CaiZhengyun Wua Y.C. J

  2. INTRODUCTION • Due to the wide band gap of SiC (4H-SiC ~3.25 eV cut-off wavelength ~380nm). • photodetectors utilizing this material should have the advantage of a good visible-blind/solar-blind performance. • very low dark current which can be many orders of magnitude lower than the dark current of conventional Si detectors.

  3. 0.38 Ω EXPERIMENT 70 nm 0.02 Ω Passivation此層用來防止漏電流 FIG. 1. Cross-sectional view (a) and top view (b) of 4H-SiC ultraviolet p-i-n photodetector.

  4. RESULTS AND DISCUSSION • A. Electrical characterization 1. Capacitance-voltage 0.7 FIG. 2. C-V characteristics i.e., 1/C2-V of the 4H-SiC p-i-n photodetector.

  5. RESULTS AND DISCUSSION • 藉由下列公式可計算出內建電壓Vbi,在所給的條件下計算出Vbi為~0.3V 藉由下列公式可計算出空乏區的寬度,在0V時W=0.6μm,而在0.7V時W=0.5um 在>0.7V對SiC之sample的i-layer空乏區寬度將變窄.

  6. RESULTS AND DISCUSSION 藉由下列公式可計算出1/C2用來描述1/C2對V的曲線電壓從0.7V到3.0V • 經由上列公式可已得到所算出的Vbi為3.0V,所量測到的為2.97±0.05V所以以符合所預估的值

  7. 在270nm的UV光照射下得到平均光電流可達6.0nA RESULTS AND DISCUSSION 2. Current-voltage 差了4個orders 12.5pA/mm2 12.5pA/mm2 FIG. 3. I-V characteristics dark current and photocurrent of the 4H-SiC p-i-n photodetector.

  8. RESULTS AND DISCUSSION 0.13 A/W • B. Photoresponse characterization 0.16 mA/W FIG. 4. The spectral responsivities of the 4H-SiC ultraviolet p-i-n photodetector under different reverse biases.

  9. RESULTS AND DISCUSSION • At wavelengths shorter than 240 nm, the quantum efficiency decreases as the wavelength decreases. • The spectrum shows a long wavelength cut off at 380 nm. At wavelengths longer than 380 nm, the 4H-SiC ultraviolet p-i-n detector shows the rarely low photoresponse. ※補充 SiC的Eg為3.25左右所以截止波長在380nm 1240/3.26=380nm

  10. RESULTS AND DISCUSSION 藉由下列公式可計算出外部量子效率 上述公式也可經由以下列公式來進行計算

  11. RESULTS AND DISCUSSION • 在270 nm時,經下列計算可以得到外部量子效率為 61 % 在380 nm時,經下列計算可以得到外部量子效率為 10-2 %

  12. CONCLUSIONS • Although 4H-SiC material is not intrinsically solar-blind, • the photodetector based on it appears to be a good potential candidate for solar-blind ultraviolet detection when employed with proper solar-blind interference filters. • solar-blind  290nm