An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. ZnO掺杂高介超宽温稳定型钛酸钡基介质材料 ------天津大学2012级硕士 报告人：陈俊晓 导　师：李玲霞 教授 专　业：微电子学与固体电子学

  2. 研究背景 片式多层陶瓷电容器的广泛应用 高介化 宽温化 小型化

  3. 研究背景 钛酸钡基介质材料 钛酸钡-钛酸铋钠基 介质材料 BT-NBT-Nb 超宽温稳定型 介质材料 +Mg2+, Zn2+, Co2+, Ni2+, Mn2+ 铅基复合钙钛矿体系 介电常数>1500 介电损耗<2.0% 电容量变化率<±15% 工作温度范围-55~300℃ 绝缘电阻率>1012Ω•cm 烧结温度<1150℃ 钨青铜矿结构体系 +Re 工艺优化

  4. BT-NBT-Nb-MO(M=Mg, Zn, Co, Ni, Mn)介质材料研究 二价金属氧化物掺杂BT-NBT-Nb [0.85BT-0.15NBT]-2wt%Nb2O5- 1.5 wt% MO M=Mg, Zn, Co, Ni, Mn 不同二价金属氧化物掺杂样品的介电性能 不同二价金属氧化物掺杂样品的介温曲线

  5. BT-NBT-Nb-MO(M=Mg, Zn, Co, Ni, Mn)介质材料研究 表五：不同摩尔含量ZnO介电性能

  6. BT-NBT-Nb-MO(M=Mg, Zn, Co, Ni, Mn)介质材料研究 1160℃烧结,1不同ZnO添加介温曲线，2电容量变化率与温度的关系 结论：ZnO添加对高介的获得提供可能。为进一步进行稀土元素掺杂改性做好准备。

  7. 总结及下一步计划 研究了二价金属氧化物掺杂对BT-NBT-Nb介质材料微观结构及介电性能的影响，分析了不同二价金属氧化物掺杂样品介电性能产生差异的原因，改善了体系高温区的温度特性。 2 在BT-NBT-Nb-Zn体系中分别加入不同含量的多种稀土氧化物，包括La2O3，CeO2，Pr6O11，Er2O3等。研究了稀土掺杂对体系的介电性能的影响。 1 下一步计划 1 主要介绍了课题研究的背景，意义，体系的选取等