An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. STUDY UPON THE GLUING SHEARING STRENGTH OF SOME ADHESIVE COMPOSITIONS BASED ON LIGNIN AND MIXED FURAN RESIN WITH FURFURYLIC ALCOHOL OF FC-2 URELIT TYPEL’ÉTUDE DE LA RÉSISTANCE DU COLLAGE AU CISAILLEMENT DE CERTAINES COMPOSITIONS ADHÉSIVES À BASE DE LIGNINE ET RÉSINE FURANNIQUE MIXTE AVEC DE L’ALCOOL FURFURYLIQUE TYPE URELIT FC-2 Prof. dr. Eng.Valeriu PETROVICI, PhD Student Eng. Anca Maria VARODI, Lecturer dr. Eng. Octavia ZELENIUC Transilvania University of Brasov, 29 Eroilor Bd., 500036, Brasov, Romania. Faculty of Wood Industry E-mail: petrovic@unitbv.ro, Tel./Fax: 0040268415315

  2. INTRODUCTION/ INTRODUCTION • Furan resins represent an important class of synthetic resins which have as starting point some chemical substances with the structure of furan type,such as: furfurol and furfurylic alcohol. • The mixed furan resins with furfurylic alcohol are well known for long, they are distinguished through certain mechanical strengths, mostly chemical and thermal ones that are higher than the phenol and amino ones. • As a result, they are still used as priority in foundries in our country, as a binder for the preparation of the mixtures and cores formation, in order to cast pieces made of cast iron, steel and other metals. • Les résines furanniques représentent une classe importante de résines synthétiques, qui ont comme point de départ certaines substances chimiques avec la structure de type furannique comme serait, par exemple, le furfurol et l’alcool furfurylique. • Les résines furanniques mixtes avec de l’alcool furfurylique sont connues depuis longtemps, elles se caractérisant par certaines résistances mécaniques chimiques et thérmiques élevées par rapport à celles phénoliques et aminiques. • À la suite de ce fait, elles sont encore utilisées surtout dans notre pays dans les fonderies, comme liant pour la préparation des mélanges de formation et des essences pour la formation des pièces en fonte, en acier et en autres métaux .

  3. INTRODUCTION/ INTRODUCTION • Elles peuvent être classifier après deux critères de base: selon la composition chimique de la catène et selon le processus de durcissement. • Selon la composition chimique de la catène ces résines peuvent étre: résines furanniques simples et résines furanniques mixtes. • Les résines furanniques mixtes avec de l’alcool furfurylique font partie elles aussi de la catégorie des résines synthétiques thermoréactives, leur réticulation ayant lieu à la température du milieu ambient au chaud, dans un fort milieu acide. • La définitivation du processus de policondensation est accompagnée par une forte deshydratation, dégagement de chaleur et de formaldéhyde. • They can be classified depending on two base criteria: the catena chemical composition and the curing procedure, respectively. • According to the catena chemical composition these resins can be: simple furan resins and mixed furan resins. • The mixed furan resins with furfurylic alcohol belong to the category of thermo-reactive synthetic resins. Their reticulation is performed at the environment temperature or when hot, under high acid conditions. • The finalization of the polycondensation process is joined by a strong dehydration, heat and formaldehyde release.

  4. INTRODUCTION/ INTRODUCTION • The reaction products resulted in this case at the resol phase are a complex mixture of short macromolecular catena, in which the monomers are bound with methylene and/or methylene-ether links, out of which one fragment could be schematically represented as follows: • Les produits de réaction résultés dans ce cas dans la phase de résol représentent, comme dans le cas des résines phénoliques et aminiques, un mélange complexe de catènes macromoléculaires courtes, où les monomères se lient entre eux par des liens méthyléniques et ou méthylène-éteriques, dont un fragment pourrait être représenté schématiquement ainsi:

  5. OBJECTIVES / OBJECTIFS • The first objective is referring to the knowledge of some aspects concerning the behavior of some adhesive compositions based on classic urea resin of URELIT R type, and mixed furan resin with furfurylic alcohol of FC-2 URELIT type when jellifying at the temperature of 20ºC. They contain similar proportions of rye flour and technical lignin as filling materials, under the conditions of using some different types and addition parts of catalysts. • The later objective consists in the determination of the gluing shearing strength in dry state and after 24 hours of water immersion at the temperature of 20ºC of those adhesive compositions, which are stipulated to be used for wood gluing at the environment temperature. • Le premièr objectif se rapporte à la connaissance de certains aspects concernant la manière de comportement à gélification à la température de 20°C de certaines compositions adhésives à base de résine uréique classique type URELIT R et la résine furannique mixte avec de l’alcool furfurylique type URELIT FC-2, qui contiennent comme matériaux de remplissement des proportions similaires de farine de seigle et de lignines téchniques, dans les conditions de l’utilisation de certains types et suppléments de catalyseurs. • Le deuxième objectif consiste dans la détermination de la résistance du collage au cisaillement en état sec et après l’immersion 24 heures dans l’eau à la température de 20°C de ces compositions adhésives, qui sont prévues à étre utilisées pour le collage du bois à la température du milieu ambient.

  6. MATERIALS AND METHODS / MATÉRIAUX ET MÉTHODES • The mixed furan resin with furfurylic alcohol of FC-2 URELIT type used within the present study is obtained through the condensation of urea with formaldehyde and furfurylic alcohol at the VIROMET Company from Victoria, Romania. • This synthetic resin is used exclusively for the abrasive fixation under different supports through reticulation at the temperature of 40ºC. • In this case, a classic urea resin of R URELIT type, manufactured by the same company, was used as control sample. This is the only one resin used nowadays in our country for wood gluing at the environment temperature. • La résine furannique mixte avec de l’alcool furfurylique type URELIT FC-2 utilisée dans cet étude est obtenue par la condensation de l’urée avec l’aldéhyde formique et l’alcool furfurylique dans le cadre de SC VIROMET SA Victoria, Roumanie. • Cette résine synthétique est destinée exclusivement pour la fixation des abrasifs sur divers supports par la réticulation à la température de 40°C. • Dans ce cas, comme échantillon on a utilisé une résine classique type URELIT R, fabriquée par le même agent économique, celle-ci étant la seule résine synthétique employée à présent dans notre pays pour le collage du bois à la température du milieu ambient .

  7. MATERIALS AND METHODS / MATÉRIAUX ET MÉTHODES Table 1: Technical quality specifications of the mixed furan resin with furfurylic alcohol URELIT FC-2 and of urea resin URELIT R, produced by SC VIROMET SA VICTORIA

  8. MATERIALS AND METHODS / MATÉRIAUX ET MÉTHODES • Within the adhesive compositions were used two types of technical lignin, generically called of GRANIT (G) and PROTOBIND (P) type as filling materials. • In this case they have integrally replaced the similar addition part of rye flour (F) from the unique recipe based on urea-formaldehyde adhesive of R URELIT type, which is used for gluing the solid wood. • Within a first category of experiments a comparative study upon the jellification process at the temperature of 20ºC of 8 adhesive compositions based on mixed furan resin with furfurylic alcohol of FC-2 URELIT type was performed. • Dans les compositions adhésives réalisées comme matériaux de remplissement on a utilisé deux types de lignines téchniques, dénommés génériquement type GRANIT (G) et type PROTOBIND (P). • Dans ce cas a été substitué intégralement le supplément de farine de seigle (F) de la recette à base d’adhésif uréo-formaldéhydique type URELIT R, employée pour le collage du bois massif. • Dans une première catégorie d’expériments on a procédé à un étude comparatif au processus de gélification à la température de 20°C de 8 compositions adhésives à base de résine furannique mixte avec de l’alcool furfurylique type URELIT FC-2.

  9. MATERIALS AND METHODS / MATÉRIAUX ET MÉTHODES • Four of them were studied when using as filling material the classic addition part of about 12.33% rye flour (F) and the other 4 with a similar addition part of sulphate technical lignin of GRANIT type (G). • In both situations, a constant addition part of about 5% IR hardener and the ammonium chloride, in solid state and in the form of aqueous solutions as well, having the concentrations of 20-25%, was used as catalyst. • Within another working stage, similar experiments concerning the jellification at the environment temperature of other 6 adhesive compositions were performed. • Dont 4 dans les conditions de l’utilisation comme matériel de remplissement du supplément classique de 12.33% farine de seigle (F), et d’autres 4 avec un supplément similaire de lignine téchnique sulfate type GRANIT (G). • Dans les deux situations on a employé comme catalyseur un supplément constant de 5% fortifiant type IR et respectivement clorure d’ammonium, en état solide et sous la forme de solutions aqueuses avec les concentrations de 20-25% . • Dans une autre étape de travail on a effectué des expériments similaires de gélification à la température du milieu ambient d’autres 6 compositions adhésives.

  10. MATERIALS AND METHODS / MATÉRIAUX ET MÉTHODES • Trois d’entre elles ont été réalisées à base de résine uréique classique type URELIT R avec le même supplément de 12,33% farine de seigle (F), lignine téchnique sulfate type GRANIT (G) et respectivement lignine téchnique sulfate type PROTOBIND (P). On a utilisé dans ce cas comme catalyseur le supplément constant de 1,5% fortifiant spécifique type IR solide. • Les trois autres compositions adhésives ont été réalisées utilisant un liant à base de résine furannique mixte avec de l’alcool furfurylique type URELIT FC-2, employant comme matériaux de remplissement le supplément similare des mêmes produits téchniques antérieurement mentionés, et comme catalyseur 5% clorure d’ammonium sous la forme d’une solution aqueuse avec la concentration de 20%. • Three of them were achieved based on classic urea resin of R URELIT type with the same addition part of about 12.33% rye flour (F), sulphate technical lignin of GRANIT (G) type and of PROTOBIND (P) type one respectively. In this case a constant addition part of 1.5% specific solid hardener of IR type was used as catalyst. • The other three adhesive compositions were achieved by using as base binder the mixed furan resin with furfurylic alcohol of FC-2 URELIT type, when using as filling materials the similar addition part of the same technical products previously mentioned and also 5% ammonium chloride in the form of aqueous solution with the concentrations of 20% as catalyst.

  11. MATERIALS AND METHODS / MATÉRIAUX ET MÉTHODES • According to the second objective, within another category of experiments, a comparative study upon the gluing shearing strength, for this adhesives in dry state and after 24 hours of water immersion at the temperature of 20 ºC was performed. • This was referring to an adhesive composition based on classic urea resin of R URELIT type in addition with rye flour, as control sample, with other two adhesive compositions using the same resin but with similar addition parts from the two types of sulphate technical lignin under study. • The same procedure was performed with an adhesive composition based on mixed furan resin with furfurylic alcohol of FC-2 URELIT type. • Conformément au deuxième objectif dans une autre catégorie d’expériments on a réalisé un étude comparatif de la résistance du collage au cisaillement, de ces adhesives en état sec et après 24 heures immersion dans l’eau à la température de 20°C. • L’ étude se refère premièrement pour une composition adhésive à base de résine uréique classique type URELIT R avec supplément de farine de seigle, comme échantillon, et pour autres deux compositions adhésives ayant la même résine, mais avec des suppléments similaires de deux types de lignines téchniques sulfate étudiées. • On a procédé de la même manière avec une composition adhésive à base de résine furannique mixte avec de l’alcool furfurylique type URELIT FC-2.

  12. RESULTS AND DISCUSSION / RÉSULTATS ET DISCUSSIONS • Les produits de réticulation qui ont èté realisées dans la prémière étape d’etude ont un aspect classique de gel transparent, de couleur jaunâtre, mais qui présente une certaine visquosité. Ce temps de gélification proprement dit, exprimé en minutes, est symbolisé dans ce cas avec “tgel”. • La durée dans laquelle les gels ainsi obtenus perdent complètement leur visquosité est distinctement évidentiée et definie à priori comme un temps de disparition de la visquosité, étant exprimé toujours en minutes et symbolisé avec “tdl”. • La troisième étape est marquée par la transformation du gel réticulé dans un produit final solide, dur et opaque, jaune, insoluble et infusible. La durée nécessaire pour atteindre cet état final de résite, est dénommée génériquement comme un temps de solidification, étant exprimée en minutes et symbolisée avec “ts”. • The reticulation products obtained during a first phase present a classic aspect of transparent gel, with a yellowish colour and certain stickiness. This jellification time, expressed in minutes, is symbolized as “tgel”. • The period when the obtained gels lose completely their stickiness, is distinctively pointed out and defined as a time of stickiness disappearance, being expressed in minutes and symbolized as “tdl”. • The third stage is marked up by the transformation of the reticulated gel through a solid, hard and opaque, yellow, insoluble and infusible final product. The time needed for reaching this final stage of resite, is generically called solidification time, being expressed in minutes and symbolized as “ts”.

  13. RESULTS AND DISCUSSION / RÉSULTATS ET DISCUSSIONS • Les données de la Figure 1 démontrent que dans le cas classique de l’utilisation comme matériel de remplissement de la farine de seigle les durées de gélification à la température de 20°C des ces 4 compositions adhésives à base de résine furannique mixte avec de l’alcool furfurylique type URELIT FC-2 sont comprise, en function du type de calatyseur utilisé, entre 28-47 minutes celles de disparition de la visquosité entre 46-66 minutes, et celles de solidification proprèment-dite entre 154-328 minutes. • Data from Figure 1 demonstrate that in the case of using the classic rye flour as filling material, the Jellification periods at the temperature of 20ºC of that four adhesive compositions based on mixed furan resin with furfurylic alcohol of FC-2 URELIT type range between 28-47 minutes, depending on the type of the used catalyst, the ones corresponding to the stickiness disappearance in between 46-66 minutes and the properly solidification ones in between 154-328 minutes.

  14. RESULTS AND DISCUSSION / RÉSULTATS ET DISCUSSIONS Fig. 2. Influence of the 5% additive of the studied catalysts upon the jellification time (tgel), stickiness disappearance time (tdl) and solidification time (ts) at the temperature of 20 ºC for the adhesive compositions based on mixed furan resin with furfurylic alcohol of FC-2 URELIT type and sulphate technical lignin of GRANIT type (G). • Dans le même contexte les représentations graphiques de la Figure 2 démontrent que les durées de gélification à la température du milieu ambient des mêmes compositions adhésives, mais réalisées avec supplément de lignine téchnique type GRANIT, sont compris entre 30-100 minutes, celles de disparition de la visquosité entre 40-60 minutes et celles de solidification finale entre 360-420 minutes. • Within the same context, the graphical representations from Figure 2 show that the jellification periods at the environment temperature of the same adhesive compositions, which are achieved by adding the technical lignin of GRANIT type, range in between 30-100 minutes, stickiness disappearance in between 40-66 minutes and that ones of final solidification in between 360-420 minutes.

  15. RESULTS AND DISCUSSION / RÉSULTATS ET DISCUSSIONS • Les représentations graphiques de Figure 3 mettent en évidence clairement le manque du phénomène de visquosité dans le cas de la gélification à la température du milieu ambient des compositions adhésives à base de résine uréique type URELIT R, celle-ci étant compris entre 24-30 minutes, indiféremment de la nature du matériel de remplissement utilisé. • Par rapport au cas de l’utilisation comme matériel de remplissement de la farine de seigle, la durée de solidification des compositions adhésives augmente avec environ 60% en utilisant le supplément de lignine téchnique sulfate type PROTOBIND et environ 134% dans le cas de type GRANIT. • The graphical representations from Figure 3 clearly highlight the lack of the stickiness phenomenon when jellifying at the environment temperature of the adhesive compositions based on urea resin of R URELIT type. This ranges in between 24-30 minutes, regardless the nature of the used filling material. • The solidification periods of these adhesive compositions are 60% increased when adding the sulphate technical lignin of PROOBIND type and 134% in the case of the technical lignin of GRANIT type, than in the case when using as filling material the rye flour.

  16. RESULTS AND DISCUSSION / RÉSULTATS ET DISCUSSIONS • Les données de la Figure 4 mettent clairement en évidence l’existence du phénomène de visquosité dans le cas de la gélification de toutes les compositions adhésives à la base de résine furannique mixte avec de l’alcool furfurylique type URELIT FC-2. • Les durées de gélification à la température de 20°C sont dans ce cas plus grandes, par rapport à celles des compositions adhésives à base de résine uréique type URELIT R, etant comprises entre 40-45 minutes, en s’inscrivant ainsi dans la valeur au maximum admissible pour cette dernière résine synthétique. • The data from Figure 4 pointed out the presence of the stickiness phenomenon during the jellification of all the adhesive compositions based on mixed furan resin with furfurylic alcohol of FC-2 URELIT type. • The jellification periods at the temperature of 20ºC are higher than that ones of the adhesive compositions based on urea resin of R URELIT type and they vary in between 40-45 minutes, being correspondent to the admissible maximum value of the last mentioned synthetic resin.

  17. RESULTS AND DISCUSSION / RÉSULTATS ET DISCUSSIONS • Les données présentées dans les deuxièmes tableaux suivants pour les 6 compositions adhésives à base de résine furannique mixte avec de l’alcool furfurylique type URELIT FC-2 et les lignines téchniques sulfate étudiées ont aussi des pH initials et finals identiques à l’échantillon similaires de réferences à base de farine de seigle. • Elles sont beaucoup plus visqueuses et presentent des durées de gélification et de disparition de la visquosité à peu près identiques. • Les résistances du collage au cisaillement en valeur absolue déterminée expérimentalement,fae,ne peuvent constituer pourtant une base réelle de comparaison, puisqu’elles correspondent à des consommations spécifiques différentes d’adhesif. • The data presented in the next two tables that the 6 adhesive compositions based on urea resin of R URELIT type and mixed furan resin with furfurylic alcohol of FC-2 URELIT type with the sulphate technical lignin under study present identical initial and final pH values with the similar control sample based on rye flour. • They are much more viscous and present almost identical jellification and stickiness disappearance times. • The gluing shearing strengths as absolute values which are experimentally determined,fae,can not form a real comparing data base, because they correspond to some different adhesive specific consumptions.

  18. RESULTS AND DISCUSSION / RÉSULTATS ET DISCUSSIONS

  19. RESULTS AND DISCUSSION / RÉSULTATS ET DISCUSSIONS

  20. RESULTS AND DISCUSSION / RÉSULTATS ET DISCUSSIONS • As a result of this fact, it was considered necessary to determine by calculus a gluing shearing strength, symbolized asfac, which is correspondent to the same specific consumption of 100g/m2 oven dry applied adhesive. • In this purpose the following relation was used (1): • Comme suite à ce fait, on a considéré nécessaire de determiner par calcul une résistance du collage au cisaillement, noté avec fac, qui doit correspondre à la même consommation spécifique de 100 g/m2 adhésif absolument sec appliqué. • Dans ce but on a employé la relation (1): (1) where:fae - the gluing shearing strength of the adhesive compositions, experimentally determined, in N/mm2; ou: -résistance du collage au cisaillement des compositions adhésives déterminée expérimentalement, en valeur absolue, en N/mm2; cspau - the specific consumption of the absolutely dry applied adhesive, in g/m2. -consommation spécifique d’adhésif absolument sec appliqué, en g/m2.

  21. RESULTS AND DISCUSSION / RÉSULTATS ET DISCUSSIONS • À la pression spécifique de 0,5 N/mm2, par exemple, les deux compositions adhésives ont des résistances du collage au cisaillement calculées qui sont plus grandes avec environ 32% en état sec et environ 97% après 24 heures d’immersion dans l’eau à la température de 20°C, dans le cas des compositions adhésives avec la lignine téchnique sulfate type GRANIT, par rapport au cas de l’utilisation comme supplément de la farine de seigle. • For the specific pressure of 0.5 N/mm2, as example, the two adhesive compositions present higher calculated gluing shearing strengthsare about 32% in dry state and about 97% after 24 hours of water immersion at the temperature of 20ºC, in the case of the adhesive compositions with sulphate technical lignin of GRANIT type, compared with rye flour as additive.

  22. RESULTS AND DISCUSSION / RÉSULTATS ET DISCUSSIONS • In the same context, for the specific pressure of 0.8 N/mm2, the growths are about 2-23% in dry state and about 37-99% after 24 hours of water immersion at the temperature of 20ºC for the adhesive compositions with addition part of sulphate technical lignin of PROTOBIND type. • Dans le même context, à la pression spécifique de 0,8N/mm2, les augmentations sont d’environ 2-23% en état sec et d’environ 37-99% après 24 heures immersion dans l’eau à la température de 20°C pour les compositions adhésives avec supplément de lignine téchnique sulfate type PROTOBIND. Fig. 6. Gluing shearing strengths calculated for the adhesive compositions based on mixed furan resin with furfurylic alcohol of FC-2 URELIT type in addition with rye flour and sulphate technical lignin studied at the pressures of 0.5 and 0.8N/mm2.

  23. RESULTS AND DISCUSSION / RÉSULTATS ET DISCUSSIONS Fig. 7. Variation of the percentage ratiofac(resin and lignin type) /facUR/IRs–F*100 for the adhesive compositions studied at the specific pressure of 0.5 N/mm2. • At the pressure of 0.5 N/mm2, as example, the gluing shearing strengths of the adhesive compositions based on furan resin with furfurylic alcohol of FC-2 URELIT type in dry state are 145% higher for the rye flour additive, 223% in the case of sulphate technical lignin of GRANIT type and about 106% for the one of PROTOBIND type. • À la pression spécifique de 0,5N/mm2, par exemple, les résistances du collage au cisaillement des compositions adhésives à base de résine furannique avec de l’alcool furfurylique type URELIT FC-2 en état sec sont plus grandes avec environ 145% pour le supplément de farine de seigle, environ 223% dans le cas du supplément de lignine téchnique sulfate type GRANIT et environ 106% pour le supplément de lignine téchnique sulfate type PROTOBIND.

  24. RESULTS AND DISCUSSION / RÉSULTATS ET DISCUSSIONS Fig. 8. Variation of the percentage ratiofac (resin and lignin type) /facUR/IRs–F*100 for the adhesive compositions studied at the specific pressure of 0.8 N/mm2. • Dans le même contexte, à la pression spécifique de 0,8N/mm2, les mêmes compositions adhésives ont des résistances du collage au cisaillement en état sec plus grandes avec 160% pour le supplément de farine de seigle, environ 168% dans le cas du supplément de lignine téchnique sulfate type GRANIT et environ 222% pour la lignine téchnique sulfate type PROTOBIND. • Within the same context, at the pressure of 0.8 N/mm2, the same adhesive compositions present in dry state higher gluing shearing strengths about 160% higher for the rye flour additive, 168% in the case of sulphate technical lignin of GRANIT type and 222% for the one of PROTOBIND type.

  25. CONCLUSIONS / CONCLUSIONS • No matter the nature of the addition part used, the catalytic effect of the four types of hardeners under study decreases respecting the following order: solid NH4Cl, solid IR, 20% solution NH4Cl and 25% IR solution. • The adhesive compositions based on urea resin of R URELIT type in addition with the three types of filling materials present almost identical physical-chemical characteristics, excepting the solidification time which is 6-8 times increased in the case of using the sulphate technical lignin. • The ones achieved and based on mixed furan resin with furfurylic alcohol of FC-2 URELIT type present identical physical-chemical characteristics as well, but being more viscous in the case of using the sulphate technical lignin of GRANIT type. The solidification time is 2 times increased only in this case. • On peut constater que si on utilise un matériel de supplément de n’importe quelle nature, l’effet catalitique des 4 types de fortifiants étudiés décroit dans l’ordre suivant: NH4Cl solide, IR solide, NH4Cl solution 20% et solution 25%. • Les compositions adhésives à base de résine uréique type URELIT R en supplément avec les trois types de matériaux presents des caractéristiques physiques et chimiques près identiques, le temps de solidification s’agrandisse dans le cas des suppléments de lignines téchniques sulfate d’environ 6-8 fois. • Celles realisées à base de résine furanniques mixte avec de l’alcool furfurylique URELIT FC-2 ont elles-aussi quelques caractéristiques physiques-chimiques identiques, étant pourtant plus visqueuses, dans le cas du supplément de lignine téchnique sulfate type GRANIT. Le temps de solidification s’agrandit dans ce cas seulement environ 2 fois.

  26. CONCLUSIONS / CONCLUSIONS • The adhesive compositions based on mixed furan resin with furfurylic alcohol of FC-2 URELIT type offer the possibility of reducing the adhesive specific consumption with about 50% than the ones based on urea resin of R URELIT type. • The adhesive compositions based on classic urea resin of R URELIT type in addition with the sulphate technical lignin of GRANIT type present the highest gluing shearing strengths, both in dry state and after 24 hours of water immersion at the temperature of 20ºC, when using a specific pressure of 0.5 N/mm2. • Les compositions adhésives à base de résine furannique mixte avec de l’alcool furfurylique type URELIT FC-2 offrent la posibilité de réduire la consommation spécifique d’adhésif avec environ 50% par rapport à celles à base de résine uréique type URELIT R. • Les compositions adhésives à base de résine uréique classique type URELIT R en supplément avec la lignine téchnique sulfate type GRANIT ont les plus grandes résistances du collage au cisaillement en état sec, mais aussi après 24 heures immersion dans l’eau à la température de 20°C dans le cas de l’utilisation de la pression spécifique de 0,5N/mm2.

  27. CONCLUSIONS / CONCLUSIONS • The ones based on sulphate technical lignin of PROTOBIND type record a favorable effect as well, but a more reduced one, in dry state at the specific pressure of 0.8 N/mm2 and when wet at the pressure of 0.5 N/mm2. • Within the same context, the adhesive compositions based on mixed furan resin with furfurylic alcohol of FC-2 URELIT type and sulphate technical lignin of GRANIT type present superior gluing shearing strengths at the pressure of 0.5 N/mm2, both in dry state and after 24 hours of water immersion at the temperature of 20ºC. • The ones with sulphate technical lignin of PROTOBIND type record a favorable effect as well in this purpose, but at the pressure of 0.8 N/mm2. • Celles à base de lignine téchnique sulfate type PROTOBIND marquent, elles aussi, un effet favorable mais plus réduit, en état sec à la pression spécifique de 0,8N/mm2 et en état humide à la pression de 0,5N/mm2. • Dans le même contexte, les compositions adhésives à base de résine furannique mixte avec de l’alcool furfurylique type URELIT FC-2 et la lignine téchnique sulfate type GRANIT ont des résistances du collage au cisaillement nettement supérieures à la pression de 0,5N/mm2 en état sec, mais aussi après 24 heures immersion dans l’eau à la température de 20°C. • Celles avec la lignine téchnique sulfate type PROTOBIND marquent elles aussi un effet favorable, mais à la pression de 0,8N/mm2.

  28. CONCLUSIONS / CONCLUSIONS • When replacing completely the rye flour with the two types of sulphate technical lignin into the adhesive compositions based on mixed furan resin with furfurylic alcohol of FC-2 URELIT type, superior gluing shearing strengths can be obtained when compared to the case of using the same compositions based on classic urea resin of R URELIT type, both in dry state and after 24 hours of water immersion at the temperature of 20ºC. • It is worth to be noticed the fact that by using the sulphate technical lignin of GRANIT type for the pressure of 0.5 N/mm2, higher gluing shearing strengths after 24 hours of water immersion at the temperature of 20ºC are obtained, being 110% higher than the ones in dry state. • En substituant intégralement la farine de seigle avec les deux types de lignines téchniques sulfate étudiés dans les compositions adhésives à base de résine furannique mixte avec de l’alcool furfurylique type URELIT FC-2 peuvent s’obtenir des résistances du collage au cisaillement, en état sec mais aussi après 24 heures immersion dans l’eau à la température de 20°C, nettement supérieures par rapport au cas des mêmes compositions à base de résine uréique classique type URELIT R. • Il faut remarquer le fait qu’ en utilisant la lignine téchnique sulfate type GRANIT dans le cas d’une pression de 0,5N/mm2 on obtient des résistances du collage au cisaillement après 24 heures immersion dans l’eau à la température de 20°C, plus grandes avec environ 110% par rapport à celles en état sec.

  29. THANK YOU FOR ATTENTION 2007 IUFRO ALL Division 5 Conference, October 29-th-November 2-nd, 2007, TAIPEI, TAIWAN.