1. CuInSe2

1. CuInSe2. Selenization in 5% H 2 Se/ Ar 400~500℃ 30~60min. In (550nm). CuInSe 2 ( 2.0 μ m). Cu (250nm). Mo (0.5 μ m). Mo. Glass. Glass. 2. Cu In x Ga 1-x Se2. Selenization in 5% H 2 Se/ Ar 400~500℃ 30~60min. In (390nm). CuIn x Ga 1-x Se 2 (2.0 μ m ). Cu 0.78 Ga 0.22 (370nm).

kaloni
Download Presentation

1. CuInSe2

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. 1. CuInSe2 Selenization in 5% H2Se/Ar 400~500℃ 30~60min. In (550nm) CuInSe2 (2.0μm) Cu (250nm) Mo (0.5μm) Mo Glass Glass 2. CuInxGa1-xSe2 Selenization in 5% H2Se/Ar 400~500℃ 30~60min. In (390nm) CuInxGa1-xSe2 (2.0μm) Cu0.78Ga0.22 (370nm) Mo (0.5μm) Mo Glass Glass ※ 상온에서 Cu-In의 Eutectic reaction을 막기 위해 CuGa합금을 증착하여 사용

More Related