Chapter 15: Polymers - Characteristics, Applications, and Processing

Chapter 15: Polymers - Characteristics, Applications, and Processing. ISSUES TO ADDRESS. • What are the tensile properties of polymers and how are they affected by basic microstructural features ?. • Hardening, anisotropy, and annealing in polymers.

malo
Download Presentation

Chapter 15: Polymers - Characteristics, Applications, and Processing

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Chapter 15:Polymers - Characteristics, Applications, and Processing ISSUES TO ADDRESS... • What are the tensile properties of polymers and how are they affected by basic microstructural features? • Hardening, anisotropy, and annealing in polymers. • How does the elevated temperature mechanical response of polymers compare to ceramics and metals? • What are the primary polymer processing methods?

  2. Mechanical Properties • i.e. stress-strain behavior of polymers brittle polymer FS of polymer ca. 10% that of metals plastic elastomer elastic modulus – less than metal Strains – deformations > 1000% possible (for metals, maximum strainca. 10% or less)

  3. Temperature and Strain Rate s (MPa) 8 0 Data for the 4°C semicrystalline 6 0 polymer: PMMA 20°C (Plexiglas) 4 0 40°C 20 to 1.3 60°C 0 0 0.1 0.2 0.3 e • Decreasing T... -- increases E -- increases TS -- decreases %EL • Increasing strain rate... -- same effects as decreasing T.

  4. fibrillar structure s (MPa) Near Failure brittle failure x near onset of failure necking plastic failure x Initial unload/reload e aligned, networked crystalline cross- case regions linked slide case semi- amorphous crystalline crystalline regions case regions align elongate Tensile Response: Brittle & Plastic

  5. Predeformation by Drawing • Drawing -- stretches the polymer prior to use -- aligns chains in the stretching direction • Results of drawing: -- increases the elastic modulus (E) in the stretching direction -- increases the tensile strength (TS) in the stretching direction -- decreases ductility (%EL) • Annealing after drawing... -- decreases alignment -- reverses effects of drawing. • Compare to cold working in metals! Is it like Strain Hardening ?

  6. Tensile Response: Elastomer s (MPa) brittle failure x plastic failure x x elastomer final: chains e are straight, still cross-linked Deformation initial: amorphous chains are is reversible! kinked, cross-linked. • Compare to responses of other polymers: -- brittle response (aligned, crosslinked & networked polymer) -- plastic response (semi-crystalline polymers)

  7. alligned chains microvoids fibrillar bridges crack Polymer Fracture – spherulites plastically deform to fibrillar structure – microvoids and fibrillar bridges form

  8. Melting vs. Glass Transition Temp. What factors affect Tm and Tg? • Both Tm and Tg increase with increasing chain stiffness • Chain stiffness increased by • Bulky sidegroups • Polar groups or sidegroups • Double bonds or aromatic chain groups • Tg is about 0.5–0.8Tm in K

  9. T Callister, rubber viscous Fig. 16.9 mobile Tm liquid tough liquid plastic Tg partially crystalline crystalline solid solid Molecular weight Dependence of polymer properties on Molecular weight and Temperature

  10. Strain-time response of materials Completely elastic Pure viscous Viscoelastic

  11. Time Dependent Deformation • Data: Large drop in Er for T > Tg. (amorphous polystyrene) 5 10 rigid solid Er(10s) (small relax) 3 10 in MPa transition tensile test 1 10 region eo strain -1 10 viscous liquid -3 s(t) (large relax) 10 60 100 140 180 T(°C) time Tg • Sample Tg(C) values: • Relaxation modulus: PE (low density) PE (high density) PVC PS PC -110 - 90 + 87 +100 +150 • Stress relaxation test: -- strain to eo and hold. -- observe decrease in stress with time.

  12. Propagation • Termination Addition (Chain) Polymerization • Initiation

  13. Condensation (Step) Polymerization

  14. Polymer Additives Improve mechanical properties, processability, durability, etc. • Fillers • Added to improve tensile strength & abrasion resistance, toughness, thermal and dimension stability & decrease cost • ex: carbon black, silica gel, wood flour, glass, limestone, etc. • Plasticizers • Improve flexibility, ductility and toughness • Added to reduce the glass transition temperature Tg • commonly added to PVC - otherwise reduction of hardness and stiffness

  15. Polymer Additives • Stabilizers • Antioxidants • UV protectants • Lubricants • Added to allow easier processing • “slides” through dies easier – ex: Na • Colorants • Dyes or pigments • Flame Retardants • Cl/F & B

  16. Thermoplastics vs. Thermosets • Thermoplastics: -- little crosslinking -- ductile -- soften with heating -- polyethylene, polypropylene, polycarbonate, polystyrene • Thermosets: -- large crosslinking (10 to 50% of mers) -- hard and brittle -- do NOT soften with heating -- vulcanized rubber, epoxies,polyester resin, phenolic resin

  17. Processing of Plastics • Thermoplastic – • can be reversibly cooled & reheated, i.e. recycled • heat till soft, shape as desired, then cool • ex: polyethylene, polypropylene, polystyrene, etc. • Thermoset • when heated forms a network • degrades (not melts) when heated • mold the prepolymer then allow further reaction • ex: urethane, epoxy

  18. Processing Plastics - Molding • Compression and transfer molding • thermoplastic or thermoset

  19. Processing Plastics - Molding • Injection molding • thermoplastic & some thermosets

  20. Processing Plastics – Extrusion

  21. Blown-Film Extrusion

  22. Processing Plastics • Blow Molding • Casting

  23. Polymer Types: Elastomers Elastomers – rubber • Crosslinked materials • Natural rubber • Synthetic rubber and thermoplastic elastomers • SBR- styrene-butadiene rubber styrene butadiene – Silicone rubber

  24. Polymer Types: Fibers Fibers - length/diameter >100 • Textiles are majority use • Must have high tensile strength • Usually highly crystalline & highly polar • Formed by spinning • ex: extrude polymer through a spinnerette • Pt plate with 1000’s of holes for nylon • ex: rayon – dissolved in solvent then pumped through die head to make fibers • the fibers are drawn • leads to highly aligned chains- fibrillar structure

  25. Polymer Types • Coatings – thin film on surface – i.e. paint, varnish • To protect item • Improve appearance • Electrical insulation • Adhesives – produce bond between two adherands • Usually bonded by: • Secondary bonds • Mechanical bonding • Films – blown film extrusion • Foams – gas bubbles in plastic

  26. Advanced Polymers • Ultrahigh molecular weight polyethylene (UHMWPE) • Molecular weight ca. 4 x 106 g/mol • Excellent properties for variety of applications • bullet-proof vest, golf ball covers, hip joints, etc. • Liquid Crystal Polymers • LCD displays UHMWPE

  27. Summary • General drawbacks to polymers: -- E, sy, Kc, Tapplication are generally small. -- Deformation is often T and time dependent. -- Result: polymers benefit from composite reinforcement. • Thermoplastics (PE, PS, PP, PC): -- Smaller E, sy, Tapplication -- Larger Kc -- Easier to form and recycle • Elastomers (rubber): -- Large reversible strains! • Thermosets (epoxies, polyesters): -- Larger E, sy, Tapplication -- Smaller Kc