A TRIAL OF REDUCING AUTOGENOUS SHRINKAGE BY RECYCLED AGGREGATE

This study investigates the use of saturated recycled aggregate to control the risk of early-age cracking in high-strength concrete. The experiment examines the effects on compressive strength, Young's modulus, splitting tensile strength, autogenous shrinkage, and self-induced stress. Results show that while autogenous shrinkage can be reduced, the use of recycled aggregate decreases compressive strength and Young's modulus. Further research is needed to optimize early-age cracking risk and compressive strength for efficient use of recycled aggregate.

Download Presentation

A TRIAL OF REDUCING AUTOGENOUS SHRINKAGE BY RECYCLED AGGREGATE

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. A TRIAL OF REDUCING AUTOGENOUS SHRINKAGE BY RECYCLED AGGREGATE Ippei Maruyama Ryoichi Sato

  2. Objective High-Strength Concrete has a risk of early age cracking due to authogenous shrinkage. How to control the risk of early-age cracking?

  3. Background • Countermeasures: • -Expansive additive • -Shrinkage-reducing agent • -C2S rich cement • Some people try to compensate the self-desiccation: • Porous lightweight aggregate • Super adsorbent polymer particle

  4. Objective 2 We use saturated recycled aggregate. Because… It is important to enhance the rate of use. -limitation of resources(natural aggregate) -shortage of dump yards -decrease of reusing for pavement or back filling

  5. Concrete Conventional High Strength Concrete 0.25 0.25 High Strength Concrete with recycled aggregate Recycled fine aggregate: 10% absorption, 30% paste in mass. Recycled coarse aggregate: 6% absorption, 40% mortar in mass.

  6. Experiment -Compressive strength -Young’s modulus -Splitting tensile strength -Autogenous shrinkage (drying shrinkage after 28 days) -Self induced stress test by beam specimen Reinforcement ratio: 1.06%, 2.39%

  7. Experiment Self-induced stress of concrete at extreme bottom fiber is calculated from the strain of rebar according to the linear strain distribution:

  8. Results (Compressive Strength, Young’s modulus) 71.2 33.3 66.1 28.3 (93%) (85%) Using recycle aggregate reduce the compressive strength and Young’s modulus.

  9. Results (Splitting Tensile strength) About 70%

  10. Results (Deformation) (40%) (120%) Using recycle aggregate reduce the autogenous shrinkage remarkably. But total shrinkage after drying of recycled concrete exceeds conventional high-strength concrete.

  11. Results (Self-induced stress) (75%) (70%) 80 1.06% 2.39% Using recycle aggregate reduce the self induced stress efficiently. This can be explained by smaller shrinkage, Young’s modulus, and larger creep.

  12. Conclusion • Using saturated recycled aggregate can reduce autogenous shrinkage. • Using recycled aggregate decrease compressive and splitting tensile strength and Young’s modulus. • Further study for optimizing the early-age cracking risk and compressive strength is necessary for efficient use of recycled aggregate.