An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. CHEM 3493 Contact Mode and Tapping Mode

  2. CdSe/ZnS QDs 10x Diluted (org. conc.=5mg/mL) 3 µm2 2 µm2 1 µm2 Topography Lateral Force

  3. CdSe/ZnS QDs 10x Diluted (org. conc.=5mg/mL; new area) 2 µm2 500 nm2 Height Profile Topography Lateral Force http://www.spectro.jussieu.fr/Optquant/Semi_conducteurs/Nanocristaux/index_nanocrystals.html Particle Size=6.3 nm

  4. PEG-silane Rings (prepared by particle lithography combined with vapor depostion) Topography 3 µm 1.5 µm 1 µm Amplitude 3 µm 1.5 µm 1 µm PEG-silane 2[METHOXY(POLYETHYLENEOXY)PROPYL]TRICHLOROSILANE Phase 3 µm 1.5 µm 1 µm

  5. PEG-silane Rings (prepared by particle lithography combined with vapor depostion) Topography Phase 250 nm 250 nm 80 nm 80 nm

  6. Nanografting (C12 SAM) Lateral Force Topography

  7. Nanografting (C12 SAM) Topography Height Profile