1 / 5

0,1

SS2506 (case hardened) 55 HRC CNGA120412-S01030A 7015. v c 165 m/min Coolant pressure 7 bar. C5-PCLNL-45065-12HP. 0,2. Cutting depth a p (mm). 0,1. Feed f n (mm/rev). 0,1. 0,15. SS2506 (case hardened) CNGA120412-S01030A 7015. v c 165 m/min Coolant pressure 35 bar.

merritt-koch
Download Presentation

0,1

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. SS2506 (case hardened) 55 HRC CNGA120412-S01030A 7015 vc165 m/min Coolant pressure 7 bar C5-PCLNL-45065-12HP 0,2 Cutting depth ap(mm) 0,1 Feed fn (mm/rev) 0,1 0,15

  2. SS2506 (case hardened) CNGA120412-S01030A 7015 vc165 m/min Coolant pressure 35 bar C5-PCLNL-45065-12HP 0,2 Cutting depth ap(mm) 0,1 Feed fn (mm/rev) 0,1 0,15

  3. Hard Part turning 60 HRC Flank wear - Dry vs HPC 70 bar Vc: 200 m/min F: 0.15 mm/r AP: 0.15 mm Insert: CNGA120412T01030AWH 7015 Holder: C6-PCLNL-45065-12HP Workpiece mat: RO169 induction – hardened to HRC 60 Dry Vb, mm 70bar Tool contact time, min

  4. Workpiece material Designation: RO 169 • Diameter: 150 mm Length: 450 mm • Chemical composition: Hardness

  5. Workpiece material Microstructure