Polarization and Strain Measurements for BaTiO 3

Polarization and Strain Measurements for BaTiO 3. 1.0 kV/mm. Sample was cycled at 0.25 kV/mm increments (from 0.25kV-2.0kV) on a triangle wave at 1Hz The coercive field of the 2.0 kV/mm loop is about 0.1 kV/mm, this value is comparable to the Jaffe of 0.3 kV/mm (<1 kV/mm)

spiro
Download Presentation

Polarization and Strain Measurements for BaTiO 3

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Polarization and Strain Measurements for BaTiO3 1.0 kV/mm • Sample was cycled at 0.25 kV/mm increments (from 0.25kV-2.0kV) on a triangle wave at 1Hz • The coercive field of the 2.0 kV/mm loop is about 0.1 kV/mm, this value is comparable to the Jaffe of 0.3 kV/mm (<1 kV/mm) • There is a difference in the remnant polarization, The sample produced in our lab had a Prof 6.17 uC/cm2 compared to about 8 uC/cm2 • Strain data show typical butterfly loops Strain (%) Polarization uC/cm2 Electric Field kV/mm Electric Field kV/mm 1.5 kV/mm Strain (%) Polarization uC/cm2 Electric Field kV/mm Electric Field kV/mm 2.0 kV/mm Strain (%) Polarization uC/cm2 Electric Field kV/mm Electric Field kV/mm “Piezoelectric Ceramics” Jaffe, 1993.

More Related