PK-1500 Technical data sheet

PK-1500 Technical data sheet. KOLON Central Research Park Electronic Materials Research Institute 2010. 11. General Properties. Exposure Energy vs. Sensitivity. Test Conditions Test Artwork : KOLON Test Artwork(Glass Mask) Lamination : 110 °C, 4kg/cm 2 , 2.0m/min

mrinal
Download Presentation

PK-1500 Technical data sheet

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. PK-1500 Technical data sheet KOLON Central Research Park Electronic Materials Research Institute 2010. 11.

  2. General Properties

  3. Exposure Energy vs. Sensitivity • Test Conditions • Test Artwork : KOLON Test Artwork(Glass Mask) • Lamination : 110 °C, 4kg/cm2, 2.0m/min • Exposure : 5Kw, collimated light • Development : 1.0wt% Na2CO3, Temp. 30 °C, Break Point 50%, Spray Pressure 1.5kg/cm2

  4. Resolution • Test Conditions • Test Artwork : KOLON Test Artwork(Glass Mask) • Lamination : 110 °C, 4kg/cm2, 2.0m/min • Exposure : 5Kw, collimated light • Development : 1.0wt% Na2CO3, Temp. 30 °C, Break Point 50%, Spray Pressure 1.5kg/cm2

  5. Adhesion • Test Conditions • Test Artwork : KOLON Test Artwork(Glass Mask) • Lamination : 110 °C, 4kg/cm2, 2.0m/min • Exposure : 5Kw, collimated light • Development : 1.0wt% Na2CO3, Temp. 30 °C, Break Point 50%, Spray Pressure 1.5kg/cm2

  6. 1/1 Resolution • Test Conditions • Test Artwork : KOLON Test Artwork(Glass Mask) • Lamination : 110 °C, 4kg/cm2, 2.0m/min • Exposure : 5Kw, collimated light • Development : 1.0wt% Na2CO3, Temp. 30 °C, Break Point 50%, Spray Pressure 1.5kg/cm2

  7. Stripping Properties • Test Conditions • Pretreatment  Lamination  Exposure  Developing  Stripping • Stripping condition: 50oC, NaOH 3.0 wt% • Test method: Dipping Method • Stripped particle size: S (small, lower than 0.5cm), M (medium, 0.5~2cm), L (large, 2~5cm), LL (extra large, larger than 5cm)

  8. SEM Images (Line/space = 40/40㎛, x400) PK-1540, 7sst /21sst PK-1540, 8sst /21sst PK-1540, 9sst /21sst (Line/space = 40/40㎛, x200) PK-1540, 7sst /21sst PK-1540, 8sst /21sst PK-1540, 9sst /21sst

  9. SEM Images (Line/space = 50/50㎛, x350) PK-1550, 8sst /21sst PK-1550, 9sst /21sst PK-1550, 10sst /21sst (Line/space = 50/50㎛, x200) PK-1550, 8sst /21sst PK-1550, 9sst /21sst PK-1550, 10sst /21sst

  10. Scum / Sludge Test • <Sludge/Scum Test condition> • Filter paper : ADVANTEC-5A • Filtering Time : Measuring after being filtered 50ml and 100ml • Sludge Weight : Measuring sludge weight after being filtered 300ml • Scum Generator : Running Time is 4hrs • temp: 30oC

  11. Scum / Sludge Test 1. Test condition. * Scum & sludge test : Na2CO3 1.0 wt% , 300mL , DFR amount 1㎡/L , 30℃, 300rpm 2. Test method. Immerse 1 m2/L of DFR to 1.0 wt% of developing solution(Na2CO3) Mechanical Stirring for 1 hrs Under yellow room Homo-mixer Stirring for 4 hrs (RPM : 3000, Temp : 30℃) After holding 1day, Check the sludge Occurred & Filtering test

  12. General Process Guideline * Clean Room: 20~22 °C, 50 ± 10 % RH